Adhesives

• Material
• Bitumen
• Bitumen and aluminium
• Fibre glass

• Full strength
• Obtained after 24 hours.

• Skin formation
• Approx. 10 min.

• Type of solvent
• Water based

• 60% strength in 20 minutes
• 20 minutes

• Adhesion
• Superior

• Appearance
• Beige foam
• White, viscous liquid
• Appearance Off-white pliable putty
• Appearance Putty like consistency of various colours
• Appearance Viscous tan liquid, drying to a beige coloured glue line
• Appearance White, trowel-able paste
• Beige trowelable mastic
• Clear viscous liquid
• Imbuia Homogenous non sag paste
• Khaki homogenous non sag paste
• Meranti Homogenous non sag paste
• Oak Homogenous non sag paste
• Off white trowelable paste
• Pale orange foam
• Pine Homogenous non sag paste
• Putty like
• Red
• Translucent yellow liquid
• Viscous white liquid

• Appearance
• Liquid, colourless to straw liquid
• White viscous liquid
• Appearance Clear, colourless liquid
• Appearance Homogenous non sag paste in grey or white
• Black
• Clear liquid
• Clear viscous liquid
• Clear, colourless viscous liquid
• Liquid
• Thick yellow liquid
• Translucent yellow liquid
• Transparent
• Yellow-amber Liquid

• Appearance and Type
• Synthetic Rubber spray

• Appearance:
• White Paste

• Appearence
• Clear, colourless viscous liquid

• Apperance
• Clear, almost colourless liquid
• Liquid
• Liquid, colorless
• Opaque liquid
• Translucent yellow liquid
• White stick
• White viscous liquid

• Apperanvce
• Epoxy-urethane hybrid

• Applicatio
• Industrial and DIY

• Application
• Interior and exterior
• Light industry, household furniture, and construction industry.
• Temperature +5 to +35 °C
• All purpose
• Automotive
• Automotive, industrial and general purpose
• Automotive, industrial and house hold
• Bolts and nuts
• Building
• Building and DIY industry
• Carpet and Vinyl
• Carpet or vinyl tiles
• Commercial and domestic
• Construction and almost every application imaginable
• Fills, seals and Insulates
• Footwear repair and DIY
• General application
• General Purpose
• General purpose
• General purpose, filling and grouting
• High strength
• Household and handcraft uses
• Household and outdoor repairs
• Ideal for home, school or office usage:
• Ideal for household repairs, DIY tasks and handicrafts
• Ideal for indoor furniture, model building and craftwork
• Ideal for industrial, home, school or office usage
• Industrial
• Industrial and DIY
• Industrial and industrial
• Interior Woodwork
• Joint sealing
• Light duty application onto internal and sheltered external walls and floors.
• Light duty on interior walls and floors.
• Locking nuts and bolts
• Multi purpose
• Multi- Purpose
• Multi purpose filling
• Multipurpose
• Multi-purpose
• Multi-Purpose
• Multi-Purpse
• Quick repairs
• Rear view mirror, glass and DIY
• Repairing
• Thread locker
• Woodblock adhesive
• Wooden tiles
• Woodwork

• Application
• General purpose
• Industrial interior and exterior use
• Shoes , leather , belts
• Wood

• Application method
• Hot melt glue gun

• Application temperature
• 18°C to 35°C

• Application temperature
• +5 to +30 °C
• Application temperature 15°C to 30°C

• Application Temperature
• 5 °C to 40 °C
• 5C to 30C

• Application temperature range
• Min. -5°C to max. +30°C

• Application temperature range
• Min. 0°C to max. 50°C

• Application Temperature:
• +5 °C to +35 °C

• Applications
• Home and industrial uses
• Security, television and general electronic cabling to walls and ceilings
• Surfaces exposed to damp, wet or underwater conditions.

• Applications
• Metal , concrete , wood and stone

• Base/Type
• Ethyl cyanoacrylate

• Boiling point/range
• Above 56 °C

• Can be cut
• 2 -5 hours

• Cap Colour
• Blue

• Cap colour
• Red
• White

• Chemical Type
• Anaerobic

• Cold Resistance
• Retains elasticity down to –30°C

• Colour
• Black
• Cherry
• Clear
• Cream
• Dries clear
• Imbuia
• Mahogany
• Natural
• Oak
• Pine
• Sapele
• White

• Colour
• Clear

• Colour – Prior to curing
• White inner / light blue outer
• White Outer / Khaki Inner

• Colour – Prior to mixing
• Blue Outer / White Inner
• Grey Outer / Black Inner

• Colour – Upon curing
• Off White
• Off White
• Steel grey
• White

• Completely dry Time
• 35 Mins

• Compressive strength at 25°C of 70 MPa
• 70 MPa

• Continous temperature Rating
• 150°C

• Continuous Temperature rating
• 150 °C

• Contious temperature rating
• 150°C

• Coverage
• Approx. 2.8m2 at 1mm thickness
• Approximately 2m2 per litre (double sided application.)
• 100ml per 200 grams
• 2m2 per litre (double sided application.)

• Coverage
• 2 to 3m2 per Lt
• Approx. 6m²/kg.
• Approximate coverage 1 m2/L. Dependent on application method.

• Coverage – 280ml cartridge
• 11 metres (5mm x 5mm joint)

• Coverage/kg
• ± 1m²/kg using a 6x6x6 notched trowel. The estimated coverage depends on the nature of the surface

• Coverage/kg
• Approximately 0.8m2 using a 6x6x6mm notched trowel

• Coverage/L
• ±4m²/L depending on the porosity of the substrate and thickness of the adhesive film

• Curing time
• Approx. 24 hours

• Curing time Approximately
• Approximately 24hours per 2mm

• Density
• 1.3 g/cm3 at 23°C
• Approx. 0.85 (g/cm3 @ 20°C)
• Approximately 1.06g/cm³
• Approximately 1.0g/cm3
• Approx. 0.840 g/cm³
• Approx. 1.38 g/cm3
• Approximately 1.10g/cm
• Density (g/cm³) 1.1

• Density
• 25-30kg/m³
• (g/cm³) 1.6
• 0.17 to 0.30Density (g/cm³)
• Approx. 0.83 g/cm3 @ 20 °C
• Approx. 0.85(g/cm3 @ 20°C)
• Approximately 0.85g/cm³
• Approximately 1.6g/cm³
• Density (g/cm³) 1.6
• Density Approx. 2.0 g/cm³
• Density Approximately 1.36g/cm³

• Density @ 20 °C
• Approx. at 0.83 g/cm3

• Density 1.62 g/cm3 at 23°C
• Density 1.62 g/cm3 at 23°C

• Density Approx
• Approx. 1.03 g/cm3

• Density Approximately 1.06g/cm³
• Approximately 1.06g/cm³

• Density:
• 1.1g/cm3

• DENSİTY: 17±2 kg/m3
• DENSİTY: 17±2 kg/m3

• Drying time
• 10 minutes to 4 hours, depending on thickness of application, temperature, humidity and surface to be treated

• Drying Time
• 2 - 5 minutes at room temperature

• Drying time
• 30 minutes
• 4 hrs

• Final cure
• 60Minutes

• Final setting time
• Approximately 24 hours at 25°C and 50% humidity

• Full cure
• 24 hours
• After 24 hours

• Full Cure
• 2 - 3 Hrs
• 24 hours

• Full cure time
• 24 Hrs

• Full Cure Time
• 24 hrs @72°F(22°C)

• Full strength
• 24 hours
• 24Hrs

• Full strength
• 1½ hour
• 30 Mins

• Full strength time
• 24 hours.

• Full tensile strength
• < 24Hrs

• Gap filling properties
• Less than 0.05 mm

• Handling bond in 4½ minutes
• 4½ minutes

• Handling bond time
• 4 Mins

• Hardens in
• 10 Mins

• Hardens in
• 10 Mins
• 40 - 60 Mins

• Heat resistance
• 90°C
• Approximately 80°c
• Up to 260ºc

• Heat Resistance
• Up to 50°C
• up to 80 °C

• Heat resistance
• –10°C -70°C
• 149°C
• 180°C
• Up to 80°C

• Heat Resistance
• Softening occurs at elevated temperatures above 45°C

• Heat resistant
• Can withstand up to 149°C.

• Heat resistant
• Can withstand up to 149°C.

• Initial boiling point and boiling range:
• >200°C

• Maimum temperature resistance
• 105°C

• Main component
• Ethyl Cyanoacrylate

• Materials bonded
• rubber, leather, carpet tiles, resin laminates, wood, hardboard, metal, canvas, linoleum, felt, cork, ceramics

• Maximum bond strength (
• Achieved after 12 hours

• Maximum Continuous high temperature
• 90°C

• Maximum Temperature resistance
• 95°C

• Melting point/freezing point:
• -22°C

• Minimum Application Temperature
• 4°C

• Minimum application temperature
• Minimum application temperature 4°C

• Oil resistance
• Very good resistance to motor oils

• pH
• Approx. 7
• 4

• PH
• 7

• PH
• Approximately 6.3
• PH Approximately 4.0

• pH:
• ~6-7

• Pressing and Clamping time
• Approx 1hr

• Product Colour
• Blue

• Product colour
• Red

• Quantity
• Quantity 10

• Ready-to-cut time
• 15-20 min.

• Recommended Gap
• 0.05 / 0.13

• Recommended gap
• 0.05-0.18

• Recommended maximum gap
• 0.02-0.25

• Service Temperature
• 5-80 °C

• Service temperature range
• Min. -10°C to Max. 80°C
• Min. –20°C to max. +80°C
• Min. -10°C to max. 70°C
• Service temperature range -5°C to + 60°C

• Service temperature range
• Min. -5°C to max. +50°C
• Min. -10°C to max. 80°C
• Up to 40 °C

• Setting time
• 10 to 60 seconds – dependent on nature of substrate, temperature, and humidity
• 24 hours, depending on temperature

• Setting time
• Approx. 24 hours depending on substrate porosity and environmental conditions
• Sets in 007
• Under 15 Seconds

• Setting/drying time
• Approximately 60 minutes according to prevailing conditions

• Size
• 1l
• 500g
• 50ml
• 50mm
• 75mm

• Size
• 3x3g

• SIze
• 500g

• Solids
• Approx. 80%

• Solids 100%
• Solids 100%

• Spread Rate
• 100-250g/m2
• 60-250g/m2

• Spread rate
• 100-250g/m2

• Spread rate
• 60-250g/m2

• State
• Pasty liquid

• Tack free time:
• Approx. 5-10 min.

• Tack off time
• Approx. 30 - 45 minutes depending on site conditions: temperature, humidity and surfaces to be treated

• Temperature Range
• -65°F to 300°F(-54°Cto 150°C

• Temperature resistance
• -40 to +90 ºC

• Temperature resistance
• Approximately -20 to 80°C

• Temperature Resistance
• Approximately -20C to 80C

• Temperature resistance up to 180°C
• Up to 180°C

• Temperature resistance
• -400ºC until +1000ºC (cured)

• Temperature Resistance:
• -40 °C to +90 °C

• Time to full cure
• 24 Hrs

• Time to initial set
• 10-18 min
• 16-26

• Time to initial set Min
• 8 - 18 Mins

• Touch dry time
• Approx. 30 minutes

• Touch dry time
• 30Min

• Touch drying
• 10-20 minutes

• Type
• Epoxy mastic
• Ethyl Cyanoacrylate Adhesive
• Polyurethane
• Polyurethane prepolymere
• Acrylic
• Cream/opaque
• Cyanoacrylate
• Epoxy
• Epoxy putty
• Epoxy-urethane hybrid
• Ethyl Cyanoacrylate
• Ethyl Cyanoacrylate Adhesive
• Expanding polyurethane foam
• Fibreglass reinforced polymer compound
• Hot melt adhesive
• Hybrid polymer
• Methacrylate adhesive
• Neoprene / polychloroprene adhesive
• Nitrile rubber solution
• Polychloroprene solvent based adhesive
• Polymer compound
• Polyurethane
• Polyurethane foam
• Polyvinyl Acetate
• Polyvinyl acetate based
• Re-usable
• Self adhesive
• Single component cyanoacrlyate based
• Solvented, rubber based sealant,
• Steel epoxy
• Synthetic rubber-based
• Toughened acrylic
• Type Natural polymer based
• Water-based synthetic ter-polymer

• Type
• Crosslinking polyvinyl acetate adhesive

• Type
• Liquid
• Polyvinyl acetate adhesive
• Type Natural polymer based
• Type Synthetic polymer base

• Type of Application
• Aerosol can

• Type Water based
• Water based

• Viscosity @ 25℃ 500
• 500

• Viscosity Paste
• Paste

• Water resistance
• Good
• Excellent
• Waterproof

• Water resistance
• Waterproof
• Good
• Waterproof

• Water Resistance
• Good
• Waterproof

• White point:
• 7° C

• Will set in about 14 minutes.
• 14Mins